Abstract This work investigated the influence of microcrystalline cellulose (MCC) in thermoplastic starch/poly (butylene adipate-co-terephthalate) films produced by blown extrusion, using different MCC contents (4, 7 and 10 g.100 g-1). The films were characterised for their mechanical, structural and barrier properties. Increasing fibres concentration reduced the tensile strength (6.9 to 4.6 MPa), the elongation at break (568 to 147%) and weight loss in water (12.8 to 11.1%) of the films. The rigidity of the films increased from 19.8 MPa (without MCC) to 79.2 MPa in the samples with 10 g.100 g-1 of MCC. SEM images showed the occurrence of some agglomerates in this sample. The water vapour permeability of the films was not affected by the presence of MCC. The production of starch/PBAT/MCC films by blown extrusion was successful; however some adjustments are necessary to improve the dispersion of the particles at the polymeric matrix.

Abstract The modification of lignocellulosic fibers can enhance their interaction with other materials and alkaline hydrogen peroxide (AHP) is a reagent widely used to promote such modification. This work aimed to modify oat hulls fibers by reactive extrusion using AHP (7 g 100 g-1 of hulls). The modified oat hulls displayed performances comparable to those observed by other researchers using conventional AHP method (without extrusion). The AHP treated oat hulls showed increased luminosity compared to the extruded ones. Fourier transform infrared spectroscopy showed differences between the modified and unmodified structures. The removal of surface compounds resulted in a more open morphology, with greater surface area and greater porosity. Reactive extrusion can be an alternative method for fiber modification with several advantages, such as short processing time and no wastewater generation.

Abstract Blends of poly(lactic acid) (PLA) and thermoplastic starch (TPS) plasticized with adipate esters (diisodecyl adipate and diethyl adipate) having different molecular weight were used to produce sheets. The calendering-extrusion process at a pilot scale was used, and the mechanical, barrier, and morphological characterization of the obtained materials were performed. The increase in the TPS content affected the mechanical properties of the sheets by increasing the elongation and decreasing the rigidity. TPS conferred a more hydrophilic character to the sheets, as observed from the water vapor permeability results. The sheets plasticized with diisodecyl adipate (DIA), having a higher molecular weight, had better mechanical and barrier properties than diethyl adipate (DEA) plasticized sheets, indicating that DIA was more effective as plasticizer. Micrographs obtained by confocal laser microscopy and scanning electron microscopy showed different morphologies when different proportions of PLA and TPS were used (dispersed or co-continuous structures), which were strongly associated with the mechanical and barrier properties.

AbstractThe demand for renewably sourced biodegradable materials has increased the need to produce materials that combine appropriate functional properties at competitive costs. Thermoplastic starch and polyester blends are an interesting alternative to current materials due to the low cost of starch and the functional properties and processability of the resulting blends. Producing thermoplastic starch (TPS) requires using a plasticiser at concentrations between 20 and 30%wt (in relation to starch). Glycerol is the most common plasticiser due to its high plasticising capacity and thermal stability at processing temperatures. The objective of this study was to evaluate glycerol waste from the biodiesel industry, with different degrees of purification, as plasticisers for TPS / poly (butylene adipate-co-terephthalate) (PBAT) blends. Different purities of glycerol produced films with similar mechanical, optical and barrier properties to those made with purified glycerol (99.7%). Therefore, crude glycerol is a renewable alternative plasticiser that reduces the cost of plasticisation by 6-fold.

The production of plant seedlings has traditionally used polyethylene bags, which are thrown out in the soil or burned after transplant because the large amount of organic material attached to the bags makes recycling difficult. Additionally, when a seedling is taken from the bag for transplant, there is the risk of root damage, which compromises the plant’s development. In this study, we developed biodegradable bags to be used in seedling production, and we verify their influence on the development of Brazilian ginseng (Pfaffia glomerata (Spreng) Pedersen), when the plant is planted without being removed from the bag. Both black and white biodegradable bags remained intact throughout the seedling production period (60 days). After being transplanted into containers (240 days), they were completely biodegraded, and there was no significant difference between the dry mass of these plants and that of plants that were transplanted without the bags. The plants that were cultivated without being removed from the polyethylene bags had root development difficulties, and the wrapping showed no signs of degradation. The use of biodegradable films is an alternative for the production of bags for seedlings, as these can then be transplanted directly into the soil without removing the bag, reducing the risk of damage to the roots during the moment of transplant.

The mechanical, viscoelastic and structural properties of starch/ poly (butylene adipate co-terephthalate) (PBAT) blown films produced by reactive extrusion were evaluated using citric acid (CA) and maleic anhydride (MA) as compatibilizers. Scanning electron microscopy images showed more homogeneous structure when CA and MA were included in the formulation. The tensile strength (MPa) was improved with the inclusion of the highest proportion of both compatibilizers (1.5 %wt). A larger elastic component with values between 0.42-0.45 for the degree of solidity (1-c1) was observed for the intermediate concentration of compatibilizers. A high level of glycerol (10 %wt) results in films with increased % elongation. Three partially miscible phases were observed in the blends. Biodegradable films of starch/PBAT with better properties could be produced by one-step reactive extrusion using CA and/or MA as compatibilizers.

Com o objetivo de avaliar a sensibilidade ao rachamento de frutos, foram realizados diferentes testes de laboratório com bagas de uva para processamento das cultivares Concord, Isabel e BRS Rúbea. Para a determinação do índice de rachamento, bagas maduras foram imersas em água destilada e avaliadas a cada hora, durante um período de dez horas. Com o auxílio de um texturômetro, foram realizados testes mecânicos. Em testes de compressão, foram avaliadas, no momento de rompimento das bagas, pressão de compressão, energia de deformação e força máxima de compressão. Com uma sonda de menor calibre, as bagas foram perfuradas, obtendo-se a força máxima de perfuração e deformação de perfuração no rompimento da película. Em testes de relaxação, foram avaliados o grau de solidez e a velocidade inicial de decaimento. Foram avaliadas também as correlações entre o índice de rachamento, e os testes mecânicos. Tanto o índice de rachamento quanto os testes mecânicos apontaram para a cultivar BRS Rúbea como a mais resistente ao rachamento e a cultivar Concord como a mais suscetível. A 'Isabel' apresentou resistência intermediária. O índice de rachamento, apresentou forte correlação com as variáveis avaliadas nos testes mecânicos e possui bom potencial para a avaliação da sensibilidade ao rachamento de materiais distintos de videira.

In order to evaluate the sensitivity of fruit cracking, different laboratory tests were performed in grape berries of the processing varieties Concord, Isabel and BRS Rubea. To determine the cracking index, ripe berries were dipped in distilled water and evaluated every hour during a period of ten hours. Mechanical tests were performed using a texturometer. In compression tests, at the cracking time, pressing pressure, strain energy, maximum force of compression and compression strain were evaluated. With a smaller diameter probe, berries were drilled to the breakup of the skin resulting in maximum force of drilling and drilling strain. In stress relaxation tests the degree of solidity and initial stress decay rate were evaluated. The correlations between the cracking index and mechanical testing were evaluated too. Both the cracking index and mechanical testing pointed to the BRS Rúbea as the most resistant to cracking and the Concord cultivar as the most susceptible. Isabel presented intermediate resistance. The cracking index showed strong correlation with the parameters evaluated in the mechanical tests and has good potential for assessing the sensitivity to cracking of different grape cultivars.